      Speciality Chemicals
 
Coatings for Electrical Grade Steels and high performance Coating
 
 
FILAMAR C-3 ORGANIC COATINGS
 
The `FILAMAR' C3-Coating system from FILTEC aims at a functionally superior and economic option to the electrical steel maker. The dual Alkyd / Polyester Phenolic system combines good punchability with hardness, without leading to flaking. The FILAMAR coatings are suitable for Cold/Hot rolled sheets in strip or coiled form. Additional options of viscosity and pigmenting of the coating, enable the users to economise on coating thickness, while retaining desired electrical performance. These coating are confirm to F class insulation material.
 
FC-300 Single component an alkyd polyester /phenolic base with melamine cross-linker. Having low solid content. Suitable for low coating thickness in its class. Applicable at low line speed.
FC-470 Single component an alkyd Polyester /phenolic base with melamine cross-linker. Having high solid content. Suitable for high coating thickness in its class. Applicable at low line speed.
CC-2002 Single component polyester base with melamine cross-linker. Having high solid content. Suitable for low to high coating thickness in its class. Applicable at higher line speed.
 
FC-300
 
DESCRIPTION FILAMAR FC-300
AISI CLASS
 C3
COATING APPEARANCE
 Copper Brown
COMPOSITION
 Single component an alkyd or polyester base with melamine cross-linker
USE RATIO
 -
pH
 > 7.5
SUITABLE LINE SPEED m/min.
 25 - 40
CURE PATTERN
 250oC PMT 1 Min.
SUITABLE FOR COATING THICKNESS µ
 1.5 - 3 µ
CONSUMPTION Kg/Ton @ 2 µ
 8-10
COATING PROPERTIES
PUNCHABILITY
 2 -3 times Bright Steel
WELDABILITY NA
IR ohm cm2/LA for 2 micron thickness >8-15
SOLVENT RESISTANCE Good
CHEMICAL RESISTANCE Good
HEAT RESISTANCE 180 °C
SRA in inert gas -
 
 
FC-470
 
DESCRIPTION FILAMAR FC-300
AISI CLASS
 C3
COATING APPEARANCE
 Copper Brown
COMPOSITION
 Single component an alkyd or polyester base with melamine cross-linker
USE RATIO
 -
pH
 > 7.5
SUITABLE LINE SPEED m/min.
 25 - 40
CURE PATTERN
 250oC PMT 1 Min.
SUITABLE FOR COATING THICKNESS µ
 3 - 7 µ
CONSUMPTION Kg/Ton @ 2 µ
 6.5 - 7
COATING PROPERTIES
PUNCHABILITY
 2 -3 times Bright Steel
WELDABILITY NA
IR ohm cm2/LA for 2 micron thickness >8-15
SOLVENT RESISTANCE Good
CHEMICAL RESISTANCE Good
HEAT RESISTANCE 180 °C
SRA in inert gas -
 
CC-2002
 
DESCRIPTION FILAMAR FC-300
AISI CLASS
 C3
COATING APPEARANCE
 Yellow Gold
COMPOSITION
 Single component an alkyd or polyester base with melamine cross-linker
USE RATIO
 -
pH
 > 7.5
SUITABLE LINE SPEED m/min.
 40 - 60
CURE PATTERN
 250oC PMT 1 Min.
SUITABLE FOR COATING THICKNESS µ
 2 - 5 µ
CONSUMPTION Kg/Ton @ 2 µ
 6.5 - 7
COATING PROPERTIES
PUNCHABILITY
 2 -3 times Bright Steel
WELDABILITY NA
IR ohm cm2/LA for 2 micron thickness >10-25
SOLVENT RESISTANCE Good
CHEMICAL RESISTANCE Good
HEAT RESISTANCE 180 °C
SRA in inert gas -
 